Ruiting MA
材料科学技术（英）
Nanocrystalline Co0.5Zn0.5Fe2O4 ferrite was synthesized by polyacrylamide gel method. The electromagnetic and microwave absorption properties of the ferrite were investigated. The results indicated that calcining temperature of the ferrite had a significant influence on the effective properties of the ferrite. When the calcining temperature was 500, 600 and 700℃, the average size of particles was 10, 30 and 80 nm, respectively. The dielectric loss (ε") and magnetic loss (u") of the ferrite was around 0.65 and 0.29 at 8.2 GHz, respectively. Microwave absorption properties of the ferrites were simultaneously influenced due to the strong correlation between reflection loss and electromagnetic parameters of the ferrite.
关键词:
Polyacrylamide gel
,
null
,
null
Ruiting MA
材料科学技术（英）
Nanocrystalline nickel zinc ferrite powders (NixZn1-xFe2O4, A for x=0, B for x=0.2, C for x=0.5, D for x=0.8 and E for x= 1) were synthesized by polyacrylamide gel method. X-ray diffraction (XRD), transmission electron microscopy (TEM) and wave-guide were used to characterize the composition. The XRD results show that the dried gel powders are amorphous, and the characteristic peaks of the spinel Ni0.5Zn0.5Fe2O4 appear after the gel is calcined at 400℃ for 1 h. When the calcining temperatures are 600 and 800℃, the average grain sizes are identified by TEM to be 10 and 30 nm, respectively. The NixZn1-xFe2O4 powders have both dielectric loss and magnetic loss in the frequency range of 8.2–11.0GHz. With the increase of Ni2+ ions content, the dielectric parameters (ε′) and permeability (u′) of the NixZn1-xFe2O4 powders decrease while the dielectric loss (ε"), magnetic loss (u") and the reflection loss increase.
关键词:
Nanocrystalline
,
ferrite
,
electromagnetic